GRÜNES SILIZIUMKARBID TYPISCHE CHEMISCHE ANALYSE [%]
| SiC |
Fe2O3 |
FC |
F.Si |
SiO2 |
GESETZ |
| 98,0-99,5 |
≤0,15 |
≤0,30 |
≤0,40 |
≤0,70 |
<0,09 |
PHYSIKALISCHE EIGENSCHAFTEN DES GRÜNEN SILIZIUMKARBIDS
| bestimmtes Gewicht |
3,95 g/cm3 |
| Mohshärte |
9.4 |
| Maximale Betriebstemperatur |
1900℃ |
| Schmelzpunkt |
2250℃ |
GRÜNE SILIZIUMCARBID- PARTIKELGRÖSSENVERTEILUNG
| F 16 |
+2000um |
0 |
+1400um |
≤20 % |
+1180um |
≥45 % |
+1180+1000um |
≥70 % |
-850um |
≤3 % |
| F20 |
+1700 um |
0 |
+1180um |
≤20 % |
+1000um |
≥45 % |
+1000+850um |
≥70 % |
-710 um |
≤3 % |
| F22 |
+1400um |
0 |
+1000um |
≤20 % |
+850 um |
≥45 % |
+850+710um |
≥70 % |
-600um |
≤3 % |
| F24 |
+1180um |
0 |
+850 um |
≤25 % |
+710 um |
≥45 % |
+710+600um |
≥65 % |
-500 um |
≤3 % |
| F30 |
+1000um |
0 |
+710 um |
≤25 % |
+600um |
≥45 % |
+600+500um |
≥65 % |
-425um |
≤3 % |
| F36 |
+850 um |
0 |
+600um |
≤25 % |
+500um |
≥45 % |
+500+425um |
≥65 % |
-355um |
≤3 % |
| F46 |
+600um |
0 |
+425um |
≤30 % |
+355 um |
≥40 % |
355+300um |
≥65 % |
-250 um |
≤3 % |
| F54 |
+500um |
0 |
+355 um |
≤30 % |
+300 um |
≥40 % |
+300+250um |
≥65 % |
-212 um |
≤3 % |
| F60 |
+425um |
0 |
+300 um |
≤30 % |
+250 um |
≥40 % |
250+212um |
≥65 % |
-180 um |
≤3 % |
| F70 |
+355 um |
0 |
+250 um |
≤25 % |
+212um |
≥40 % |
+212+180um |
≥65 % |
-150um |
≤3 % |
| F80 |
+300 um |
0 |
+212um |
≤25 % |
+180 um |
≥40 % |
+180+150um |
≥65 % |
-125 um |
≤3 % |
| F90 |
+250 um |
0 |
+180 um |
≤20 % |
+150 um |
≥40 % |
+150+125um |
≥65 % |
-106 um |
≤3 % |
| F100 |
+212um |
0 |
+150 um |
≤20 % |
+125um |
≥40 % |
+125+106um |
≥65 % |
-75um |
≤3 % |
| F120 |
+180 um |
0 |
+125um |
≤20 % |
≥40 % |
≥40 % |
+106+90um |
≥65 % |
-63um |
≤3 % |
| F150 |
+150 um |
0 |
+106um |
≤15 % |
+75um |
≥40 % |
+75+63um |
≥65 % |
-45um |
≤3 % |
| F180 |
+125um |
0 |
+90um |
≤15 % |
+75um |
* |
+75+63um |
≥40 % |
-53um |
* |
| F220 |
+106um |
0 |
+75um |
≤15 % |
+63um |
* |
+63+53um |
≥40 % |
-45um |
* |
GRÜNES SILIZIUMKARBID KAPITEL Ⅰ (JIS STANDARD)
| Größe |
TUN(eins) |
D3(ähm) |
D50 (eins) |
D94(um) |
| #240 |
≤127 |
≤103 |
57,0 ± 3,0 |
≥40 |
| #280 |
≤112 |
≤87 |
48,0 ± 3,0 |
≥33 |
| #320 |
≤98 |
≤74 |
40,0 ± 2,5 |
≥27 |
| #360 |
≤86 |
≤66 |
35,0 ± 2,0 |
≥23 |
| #400 |
≤75 |
≤58 |
30,0 ± 2,0 |
≥20 |
| #500 |
≤63 |
≤50 |
25,0 ± 2,0 |
≥16 |
| #600 |
≤53 |
≤41 |
20,0 ± 1,5 |
≥13 |
| #700 |
≤45 |
≤37 |
17,0 ± 1,5 |
≥11 |
| #800 |
≤38 |
≤31 |
14,0 ± 1,0 |
≥9,0 |
| #1000 |
≤32 |
≤27 |
11,5 ± 1,0 |
≥7,0 |
| #1200 |
≤27 |
≤23 |
9,5 ± 0,8 |
≥5,5 |
| #1500 |
≤23 |
≤20 |
8,0 ± 0,6 |
≥4,5 |
| #2000 |
≤19 |
≤17 |
6,7 ± 0,6 |
≥4,0 |
| #2500 |
≤16 |
≤14 |
5,5 ± 0,5 |
≥3,0 |
| #3000 |
≤13 |
≤11 |
4,0 ± 0,5 |
≥2,0 |
| #4000 |
≤11 |
≤8,0 |
3,0 ± 0,4 |
≥1,8 |
| #6000 |
≤8,0 |
≤5,0 |
2,0 ± 0,4 |
≥0,8 |
| #8000 |
≤6,0 |
≤3,5 |
1,2 ± 0,3 |
≥0,6 |
GRÜNES SILIZIUMKARBID KAPITEL Ⅱ (FEPA STANDARD)
| Größe |
D3(ähm) |
D50 (eins) |
D94（um) |
| F230 |
<82 |
53,0 ± 3,0 |
>34 |
| F240 |
<70 |
44,5 ± 2,0 |
>28 |
| F280 |
<59 |
36,5 ± 1,5 |
>22 |
| F320 |
<49 |
29,2 ± 1,5 |
>16,5 |
| F360 |
<40 |
22,8 ± 1,5 |
>12 |
| F400 |
<32 |
17,3 ± 1,0 |
>8 |
| F500 |
<25 |
12,8 ± 1,0 |
>5 |
| F600 |
<19 |
9,3 ± 1,0 |
>3 |
| F800 |
<14 |
6,5 ± 1,0 |
>2 |
| F1000 |
<10 |
4,5 ± 0,8 |
>1 |
| F1200 |
<7 |
3,0 ± 0,5 |
>1(bei80%) |
| F1500 |
<5 |
2,0 ± 0,4 |
>0,8 (bei 80 %) |
| F2000 |
<3,5 |
1,2 ± 0,3 |
>0,5 (bei 80 %) |
GRÜNES SILIZIUMKARBID Hauptsächliche Anwendungen
- Gebundene Schleifmittel und beschichtete Schleifmittel
- Strahlen, Oberflächenbehandlung, Rostentfernung
- Nass- und Trockenstrahlmittel, Schleifen und Polieren usw
- Boden-/Wandlaminate, verschleißfest
- Keramikprodukte: Keramik und Fliesen, Keramikfilterplatte, Keramikmembran usw
- Teflonlackierung usw
- Wärmeisolierendes Material
- Schleifscheiben, Topfscheiben, Schleifstein, Polierpads usw
- Wird für Tiegel, Teile für Brennöfen, mechanische Dichtungen und Teilematerialien zur Herstellung von Halbleitern verwendet
VERPACKUNG:
25 kg PVC-Beutel + 1 m großer Beutel,
25 kg PVC-Beutel + Palette