Schwarzes Siliziumkarbid F150TYPISCHE CHEMISCHE ANALYSE [%]
SiC | Fe2O3 | FC | F.Si | SiO2 | GESETZ |
≥98,5 % | ≤0,15 | ≤0,30 | ≤0,40 | ≤0,70 | < 0,09 |
Schwarzes Siliziumkarbid F150 PHYSIKALISCHE EIGENSCHAFTEN
Bestimmtes Gewicht | 3,95 g/cm³ |
Mohs-Härte | 9.15 |
Maximale Betriebstemperatur | 1900℃ |
Schmelzpunkt | 2250℃ |
Schwarzes Siliziumkarbid PARTIKELGRÖSSENVERTEILUNG
F008 | +4000 um | 0 | +2800 um | ≤20% | +2360 um | ≥45% | +2360+2000um | ≥70% | -1700 um | ≤3% |
F010 | +3350 um | 0 | +2360 um | ≤20% | +2000 um | ≥45% | +2000+1700um | ≥70% | -1400 um | ≤3% |
F012 | +2800 um | 0 | +2000 um | ≤20% | +1700 um | ≥45% | +1700+1400um | ≥70% | -1180 um | ≤3% |
F014 | +2360 um | 0 | +1700 um | ≤20% | +1400 um | ≥45% | +1400+1180um | ≥70% | -1000 um | ≤3% |
F016 | +2000 um | 0 | +1400 um | ≤20% | +1180um | ≥45% | +1180+1000um | ≥70% | -850 um | ≤3% |
F020 | +1700 um | 0 | +1180um | ≤20% | +1000 um | ≥45% | +1000+850um | ≥70% | -710 um | ≤3% |
F022 | +1400 um | 0 | +1000 um | ≤20% | +850um | ≥45% | +850+710um | ≥70% | -600 um | ≤3% |
F024 | +1180um | 0 | +850um | ≤25% | +710um | ≥45% | +710+600um | ≥65% | -500 um | ≤3% |
F030 | +1000 um | 0 | +710um | ≤25% | +600 um | ≥45% | +600+500um | ≥65% | -425um | ≤3% |
F036 | +850um | 0 | +600 um | ≤25% | +500 um | ≥45% | +500+425um | ≥65% | -355 um | ≤3% |
F046 | +600 um | 0 | +425um | ≤30% | +355um | ≥40% | 355+300um | ≥65% | -250 um | ≤3% |
F054 | +500 um | 0 | +355um | ≤30% | +300 um | ≥40% | +300+250um | ≥65% | -212 um | ≤3% |
F060 | +425um | 0 | +300 um | ≤30% | +250um | ≥40% | 250+212um | ≥65% | -180um | ≤3% |
F070 | +355um | 0 | +250um | ≤25% | +212 um | ≥40% | +212+180um | ≥65% | -150 um | ≤3% |
F080 | +300 um | 0 | +212 um | ≤25% | +180 um | ≥40% | +180+150um | ≥65% | -125um | ≤3% |
F090 | +250um | 0 | +180 um | ≤20% | +150um | ≥40% | +150+125um | ≥65% | -106um | ≤3% |
F100 | +212 um | 0 | +150um | ≤20% | +125 um | ≥40% | +125+106um | ≥65% | -75 um | ≤3% |
F120 | +180 um | 0 | +125 um | ≤20% | ≥40% | ≥40% | +106+90um | ≥65% | -63 um | ≤3% |
F150 | +150um | 0 | +106um | ≤15% | +75 um | ≥40% | +75+63um | ≥65% | -45 um | ≤3% |
F180 | +125 um | 0 | +90 um | ≤15% | +75 um | * | +75+63um | ≥40% | -53 um | * |
F220 | +106um | 0 | +75 um | ≤15% | +63um | * | +63+53um | ≥40% | -45 um | * |
Schwarzes Siliziumkarbid KAPITEL Ⅰ (JIS-STANDARD)
Größe | TUN (eins) | D3 (ähm) | D50 (eins) | D94(um) |
#240 | ≤127 | ≤103 | 57,0±3,0 | ≥40 |
#280 | ≤112 | ≤87 | 48,0±3,0 | ≥33 |
#320 | ≤98 | ≤74 | 40,0 ± 2,5 | ≥27 |
#360 | ≤86 | ≤66 | 35,0 ± 2,0 | ≥23 |
#400 | ≤75 | ≤58 | 30,0 ± 2,0 | ≥20 |
#500 | ≤63 | ≤50 | 25,0 ± 2,0 | ≥16 |
#600 | ≤53 | ≤41 | 20,0 ± 1,5 | ≥13 |
#700 | ≤45 | ≤37 | 17,0 ± 1,5 | ≥11 |
#800 | ≤38 | ≤31 | 14,0 ± 1,0 | ≥9,0 |
#1000 | ≤32 | ≤27 | 11,5 ± 1,0 | ≥7,0 |
#1200 | ≤27 | ≤23 | 9,5 ± 0,8 | ≥5,5 |
#1500 | ≤23 | ≤20 | 8,0 ± 0,6 | ≥4,5 |
#2000 | ≤19 | ≤17 | 6,7 ± 0,6 | ≥4,0 |
#2500 | ≤16 | ≤14 | 5,5 ± 0,5 | ≥3,0 |
#3000 | ≤13 | ≤11 | 4,0 ± 0,5 | ≥2,0 |
#4000 | ≤11 | ≤8,0 | 3,0 ± 0,4 | ≥1,8 |
#6000 | ≤8,0 | ≤5,0 | 2,0 ± 0,4 | ≥0,8 |
#8000 | ≤6,0 | ≤3,5 | 1,2 ± 0,3 | ≥0,6 |
Schwarzes Siliziumkarbid KAPITEL Ⅱ (FEPA-STANDARD)
Größe | D3 (ähm) | D50 (eins) | D94(um) |
F230 | <82 | 53,0 ± 3,0 | >34 |
F240 | <70 | 44,5 ± 2,0 | >28 |
F280 | <59 | 36,5 ± 1,5 | >22 |
F320 | <49 | 29,2 ± 1,5 | >16.5 |
F360 | <40 | 22,8 ± 1,5 | >12 |
F400 | <32 | 17,3 ± 1,0 | >8 |
F500 | <25 | 12,8 ± 1,0 | >5 |
F600 | <19 | 9,3 ± 1,0 | >3 |
F800 | <14 | 6,5 ± 1,0 | >2 |
F1000 | <10 | 4,5 ± 0,8 | >1 |
F1200 | <7 | 3,0 ± 0,5 | >1 (bei 80%) |
F1500 | <5 | 2,0 ± 0,4 | >0,8 (bei 80 %) |
F2000 | <3.5 | 1,2 ± 0,3 | >0,5 (bei 80 %) |
HAUPTANWENDUNGEN VON SCHWARZEM SILIZIUMKARBID
- Gebundene Schleifmittel und Schleifmittel auf Unterlage
- Strahlen, Oberflächenbehandlung, Entrostung
- Nass- und Trockenstrahlmittel, Schleifen und Polieren etc
- Boden-/Wandlaminate, verschleißfest
- Keramische Produkte: Keramik und Fliesen, Keramikfilterplatte, Keramikmembran usw
- Teflonanstrich etc
- Wärmeisolierendes Material
- Schleifscheiben, Topfscheiben, Wetzsteine, Polierpads etc
- Verwendet für Tiegel, Teile für Ofenbrennen, Gleitringdichtungen und Teilematerialien zur Herstellung von Halbleitern